ASTM A202 Grade B is a chromium-manganese-silicon low-alloy steel tailored for high-pressure, medium-temperature pressure vessel applications.2026-04-30
-
ASTM A202 Grade A is a critical chromium-manganese-silicon low-alloy steel plate specifically designed for welded pressure vessels and boilers operating at medium temperatures.2026-04-30
-
ASTM A202 Pressure Vessel Steel Material and Grades:
Alloy System: **Chromium-Manganese-Silicon (Cr-Mn-Si)** Low-Alloy Heat-Resistant Steel2026-04-17 -
ASTM A204/A204M Grade B molybdenum alloy steel plates for pressure vessels feature superior chemical composition and mechanical properties compared to Grade A2026-04-10
-
As a molybdenum-alloy steel plate for pressure vessels under the ASTM A204/A204M standard, A204 Gr.A is a low-alloy, high-strength material specifically designed for service conditions involving moderate temperatures (≤400°C) and moderate-to-high pressure2026-03-31
EN 10028-3 P355NL2 steel,EN 10028-3 P355NL2 steel Tensile Requirements
EN 10028-3 P355NL2 steel has a more tightly controlled Phosphorus and Sulphur content.
EN 10028-3 P355NL2 steel has higher required impact values at all specified temperatures and in both longitudinal and transverse directions. EN 10028-3 P355NL2 steel also specifies requirements for transverse impact testing at -50 deg C.
EN 10028-3 P355NL2 steel Chemical Requirements:
|
Grade |
C |
Si |
Mn |
P |
S |
Altotal |
N |
Cr |
|
P355NL2 |
0.18 |
0.50 |
1.10-1.70 |
0.020 |
0.005 |
0.020 min |
0.012 |
0.30 |
|
Grade |
Cu |
Mo |
Nb |
Ni |
Ti |
V |
Nb+Ti+V |
|
|
P355NL2 |
|
|
|
|
|
|
|
|
EN 10028-3 P355NL2 steel Tensile Requirements:
|
Product Thickness |
Yield Strength MPa |
Tensile Strength MPa |
Elongation A% |
|
up to 16 mm |
355 min |
490 to 630 |
22 min |
|
16 to 40 mm |
345 min |
490 to 630 |
22 min |
|
over 40 to 60 mm |
335 min |
490 to 630 |
22 min |
|
over 60 to 100 mm |
315 min |
470 to 610 |
21 min |
|
over 100 to 150 mm |
305 min |
460 to 600 |
21 min |
|
over 150 to 250 mm |
295 min |
450 to 590 |
21 min |
EN 10028-3 P355NL2 steel Impact energy values for the normalised condition:
transverse
|
Steel Grade |
-50 oC |
-40 oC |
-20 oC |
0 oC |
+20 oC |
|
P355NL2 |
27 J min |
30 J min |
40 J min |
60 J min |
70 J min |
longitudinal
|
Steel Grade |
-50oC |
-40oC |
-20oC |
0 oC |
+20oC |
|
P355NL2 |
42 J min |
45 J min |
55 J min |
75 J min |
85 J min |