ASTM A202 Grade B is a chromium-manganese-silicon low-alloy steel tailored for high-pressure, medium-temperature pressure vessel applications.2026-04-30
-
ASTM A202 Grade A is a critical chromium-manganese-silicon low-alloy steel plate specifically designed for welded pressure vessels and boilers operating at medium temperatures.2026-04-30
-
ASTM A202 Pressure Vessel Steel Material and Grades:
Alloy System: **Chromium-Manganese-Silicon (Cr-Mn-Si)** Low-Alloy Heat-Resistant Steel2026-04-17 -
ASTM A204/A204M Grade B molybdenum alloy steel plates for pressure vessels feature superior chemical composition and mechanical properties compared to Grade A2026-04-10
-
As a molybdenum-alloy steel plate for pressure vessels under the ASTM A204/A204M standard, A204 Gr.A is a low-alloy, high-strength material specifically designed for service conditions involving moderate temperatures (≤400°C) and moderate-to-high pressure2026-03-31
S235J2 Carbon steel plate mechanical property
S235J2 steel is a low carbon, high tensile strength structural steel that under the EN 10025-s standard. It is readily welded to other weld-able steel.
With its low carbon equivalent, S235J2 steel possesses good cold-forming properties. The S235J2 steel plate is produced by fully killed steel process, and supplied in normalized or controlled rolling condition.
Production Size: Thickness: 4mm- 400mm; Width: 1000mm- 4000mm; Length: 4000mm- 12000mm.
S235J2 Carbon steel plate Mechanical Properties:
|
Grade
|
Thickness |
Min Yield |
Tensile |
Min Impact |
|
|
S235J2 |
8mm-100mm |
215Mpa-235Mpa |
360-510Mpa |
-20 |
27J |
|
101mm-200mm |
185-195Mpa |
350-490Mpa |
-20 |
27J |
|
|
201mm-400mm |
165-175Mpa |
330-480 |
-20 |
27J |
|
To learn more about S235J2 Carbon steel plate, contact us at any time. We are look forward to establishing a good and long-term business relationship with you.