ASTM A202 Grade B is a chromium-manganese-silicon low-alloy steel tailored for high-pressure, medium-temperature pressure vessel applications.2026-04-30
-
ASTM A202 Grade A is a critical chromium-manganese-silicon low-alloy steel plate specifically designed for welded pressure vessels and boilers operating at medium temperatures.2026-04-30
-
ASTM A202 Pressure Vessel Steel Material and Grades:
Alloy System: **Chromium-Manganese-Silicon (Cr-Mn-Si)** Low-Alloy Heat-Resistant Steel2026-04-17 -
ASTM A204/A204M Grade B molybdenum alloy steel plates for pressure vessels feature superior chemical composition and mechanical properties compared to Grade A2026-04-10
-
As a molybdenum-alloy steel plate for pressure vessels under the ASTM A204/A204M standard, A204 Gr.A is a low-alloy, high-strength material specifically designed for service conditions involving moderate temperatures (≤400°C) and moderate-to-high pressure2026-03-31
P460NL1 steel plate specification,P460NL1 steel plate supplier
P460NL1 steel plate under EN 10028-3 standard, it is a kind of high yield pressure vessels steel. P460NL1 shall be done low temperature impacting test at Minus 40 centi degree. More information about P460NL1 steel plate, please see the following:
|
C |
Si |
Mn |
P |
S |
Al total |
N |
Cr |
|
0.20 |
0.60 |
1.10-1.70 |
0.025 |
0.015 |
0.020 min |
0.025 |
0.30 |
|
Cu |
Mo |
Nb |
Ni |
Ti |
V |
Nb+Ti+V |
|
|
0.70 |
0.10 |
0.05 |
0.80 |
0.03 |
0.20 |
0.22 |
|
|
Product Thickness |
Yield Strength MPa |
Tensile Strength MPa |
Elongation A% |
|
up to 16 mm |
460 min |
570 to 730 |
17 min |
|
16 to 40 mm |
445 min |
570 to 720 |
17 min |
|
over 40 to 60 mm |
430 min |
570 to 720 |
17 min |
|
over 60 to 100 mm |
400 min |
540 to 710 |
17 min |
|
-50 OC |
-40 OC |
-20 OC |
0 OC |
+20 OC |
|
- |
27 J min |
35 J min |
50 J min |
60 J min |
|
-50oC |
-40oC |
-20oC |
0 OC |
+20oC |
|
30 J min |
40 J min |
50 J min |
70 J min |
80 J min |