ASTM A202 Grade B is a chromium-manganese-silicon low-alloy steel tailored for high-pressure, medium-temperature pressure vessel applications.2026-04-30
-
ASTM A202 Grade A is a critical chromium-manganese-silicon low-alloy steel plate specifically designed for welded pressure vessels and boilers operating at medium temperatures.2026-04-30
-
ASTM A202 Pressure Vessel Steel Material and Grades:
Alloy System: **Chromium-Manganese-Silicon (Cr-Mn-Si)** Low-Alloy Heat-Resistant Steel2026-04-17 -
ASTM A204/A204M Grade B molybdenum alloy steel plates for pressure vessels feature superior chemical composition and mechanical properties compared to Grade A2026-04-10
-
As a molybdenum-alloy steel plate for pressure vessels under the ASTM A204/A204M standard, A204 Gr.A is a low-alloy, high-strength material specifically designed for service conditions involving moderate temperatures (≤400°C) and moderate-to-high pressure2026-03-31
Hot rolled JIS S55C Carbon structural steel plate in stock
JIS S55C is one mainly of Carbon structural steel. JIS S55C steel plate have good wear resistance, ductility decreases, quenching distortion and cracking easily. It is also a kind of Quenched and subsequently tempered steel for screws, forgings, wheel-tyres, shafts, sickles, axes, knives, etc.
Chemical Composition of JIS S55C steel plate:
|
Grade
|
C |
Si |
Mn |
P |
S |
Cr |
|
S55C |
0.52-0.60 |
0.15-0.35 |
0.60-0.90 |
0.025 |
0.025 |
0.20-0.40 |
JIS S55C Carbon structural steel plate mechanical properties:
Tensile strength σb (MPa)(min):735
Yield strength σs (MPa)(min):372
elongation δ5 (%)(min):22
percentage reduction of area ψ (%)(min):38
impact energy Akv (J)(min): 35
compressive strength(Mpa)(min): 350
If you want to know more about JIS S55C steel plate specification, JIS S55C steel plate price, please contact with us.